ABS KINGFA HITOY-200 S9W-T6600

ABS KINGFA HITOY-200 S9W-T6600

ABS KINGFA HITOY-200 S9W-T6600 is a general-grade Acrylonitrile Butadiene Styrene (ABS) resin manufactured by KINGFA Science & Technology Co., Ltd[cite: 16]. Characterized by well-balanced mechanical properties, high rigidity, good impact resistance, and versatile processability, HITOY-200 S9W-T6600 is an optimal choice for injection molding applications across toys, home appliances, office equipment, and automotive components[cite: 16].

Key Features

• Balanced Performance Profile: Combines excellent rigidity, toughness, and thermal properties for wide application versatility[cite: 16].
• Good Mechanical Strength with a flexural modulus of 2500 MPa and tensile strength of 45 MPa[cite: 16].
• Reliable Impact Resistance with an Izod notched impact strength of 23 kJ/m²[cite: 16].
• UL 94 HB Flammability Rating at both 1.6 mm and 0.8 mm thickness[cite: 16].
• Consistent Moldability with a low mold shrinkage rate (0.4% – 0.7%) for dimensional stability[cite: 16].

Technical Specifications

• Product Name: General Grade ABS Resin[cite: 16]
• Grade / Color Code: HITOY-200 S9W-T6600[cite: 16]
• Manufacturer: KINGFA Science & Technology Co., Ltd.[cite: 16]
• Density (ISO 1183-1, 23°C): 1.05 g/cm³[cite: 16]
• Melt Mass-Flow Rate (ISO 1133-1): 2.0 g/10min (200°C / 5 kg) | 20 g/10min (220°C / 10 kg)[cite: 16]
• Tensile Strength (ISO 527-2, 50 mm/min): 45 MPa[cite: 16]
• Tensile Strain at Break (ISO 527-2, 50 mm/min): 25%[cite: 16]
• Flexural Strength (ISO 178, 2 mm/min): 71 MPa[cite: 16]
• Flexural Modulus (ISO 178, 2 mm/min): 2500 MPa[cite: 16]
• Izod Notched Impact Strength (ISO 180, 23°C): 23 kJ/m²[cite: 16]
• Rockwell Hardness (ISO 2039-2): 108 (R-Scale)[cite: 16]
• Heat Deflection Temperature (ISO 75-2): 85°C (0.45 MPa) | 77°C (1.8 MPa)[cite: 16]
• Vicat Softening Temperature (ISO 306): 102°C (1 kg, 120°C/h) | 97°C (5 kg, 50°C/h)[cite: 16]
• Volume Resistivity (IEC 60093): 10¹⁴ Ω·cm[cite: 16]
• Dielectric Strength (IEC 60243-1): 22 kV/mm[cite: 16]
• Molding Shrinkage (ISO 2577, 23°C): 0.4% – 0.7%[cite: 16]
• Flammability Rating (UL 94): HB (1.6 mm / 0.8 mm)[cite: 16]

Applications

• Toys and recreational products[cite: 16]
• Home appliances and housing enclosures[cite: 16]
• Automotive interior and exterior components[cite: 16]
• Office equipment and consumer electronics[cite: 16]

Recommended Processing Conditions (Injection Molding)

• Pre-Drying Requirements: 80°C – 90°C for 2 – 4 hours prior to processing[cite: 16].
• Melt Temperature: Optimum 215°C (Range: 200°C – 230°C)[cite: 16].
• Barrel Zone Temperatures: Rear 190°C (180–200°C) | Center 200°C (190–210°C) | Front 210°C (195–220°C)[cite: 16].
• Mold Temperature: Optimum 50°C (Range: 30°C – 60°C)[cite: 16].
• Processing Temperature Upper Limit: 250°C[cite: 16].
• Injection Speed: Slow to Moderate[cite: 16].
• Back Pressure: 0 – 1000 kPa[cite: 16].

Note: Reported physical properties reflect typical test values from the manufacturer (TDS revision dated Feb 3, 2024)[cite: 16]. Store resin away from direct sunlight to prevent yellowing caused by UV exposure[cite: 16].