RECYCLE PP BENING

RECYCLE PP BENING

RECYCLE PP BENING is a high-purity recycled polypropylene (r-PP) pellet grade specifically developed for injection molding applications. Sourced from post-industrial and post-consumer clear PP plastic streams, this recycled resin offers good natural clarity, a balanced melt flow profile, and reliable mechanical properties, making it an eco-friendly and cost-effective alternative to virgin PP resins.

Key Features

• Eco-Friendly Sustainable Option: Derived from recycled transparent polypropylene material to support circular economy initiatives.
• Good Natural Clarity: High visual transparency suited for clear or lightly tinted molded plastic products.
• Injection Molding Grade: Formulated with optimal melt flow behavior for smooth cavity filling and efficient cycle times.
• Balanced Mechanical Strength: Delivers a good combination of stiffness, impact strength, and structural integrity.
• Cost-Effective Performance: Lowers raw material costs while maintaining reliable performance in non-critical applications.

Technical Specifications

• Product Name: Recycle PP Bening (r-PP Clear)
• Product Category: Polypropylene / Recycled PP (r-PP)
• Processing Method: Injection Molding
• Appearance: Clear / Natural Transparent Pellets
• Base Material: Recycled Polypropylene Homopolymer / Copolymer
• Density: ~0.90 – 0.91 g/cm³
• Melt Flow Index (MFI @ 230°C / 2.16 kg): ~8 – 15 g/10min (Typical)

Applications

• Clear plastic containers, storage boxes, and organizers
• Consumer goods housings, housewares, and utility trays
• Caps, closures, hanger products, and general plastic components
• Compounding base resin for recycled polyolefin masterbatches

Processing & Storage Guidelines

• Drying Recommendation: If moisture accumulation is observed, pre-drying at 70°C – 80°C for 1 to 2 hours is recommended prior to molding.
• Storage Conditions: Store in a cool, dry place away from direct UV exposure, excessive heat, and moisture contamination.

Note: As this product is derived from recycled material streams, slight batch-to-batch variations in melt flow and clarity may occur. Users are advised to run preliminary production trials to confirm processing suitability.