RED MASTERBATCH 2100

RED MASTERBATCH 2100

RED MASTERBATCH 2100 is a premium color masterbatch manufactured by PT Samjin Polytech Indonesia[cite: 21]. Formulated with a polyethylene (PE) carrier resin and high-quality red pigments, 2100 is engineered to provide vibrant, uniform red coloring for polyolefin applications, including Polyethylene (PE) and Polypropylene (PP) products[cite: 21].

Key Features

• Delivers consistent, high-opacity red pigmentation for PE and PP resins[cite: 21].
• High Melt Flow Rate (24 g/10min) ensuring superior extrusion fluidity and high-speed processing[cite: 21].
• Features excellent pigment dispersion and thermal stability during extrusion and molding processes[cite: 21].
• Low moisture content (below 0.3%) to ensure smooth processing without surface defects[cite: 21].
• Standard recommended dosage rate of 3% by weight for cost-effective color consistency[cite: 21].

Technical Specifications

• Product Name: Red Masterbatch #2100[cite: 21]
• Article Code: #2100[cite: 21]
• Manufacturer: PT Samjin Polytech Indonesia[cite: 21]
• Carrier Resin: PE (Polyethylene)[cite: 21]
• Color / Appearance: Red Pellets[cite: 21]
• Melting Point: 110°C – 115°C[cite: 21]
• Melt Flow Rate (MFR) (190°C / 2.16 kg): 24 g/10min[cite: 21]
• Specific Gravity: 1.47[cite: 21]
• Moisture Content: Below 0.3%[cite: 21]
• Recommended Dosage: 3% (wt)[cite: 21]
• Packaging: 25 kg Bag[cite: 21]

Applications

• PE & PP Film Extrusion (blown film, cast film)[cite: 21]
• Injection Molding of polyolefin consumer and industrial products[cite: 21]
• Blow Molding for containers and hollow packaging[cite: 21]
• Profile and straw extrusion[cite: 21]

Storage & Handling Guidelines

• Shelf Life: 12 months when stored in unopened original containers[cite: 21].
• Storage Conditions: Keep in a cool, dry place under a maximum temperature of 35°C[cite: 21].
• Protection: Avoid direct exposure to sunlight[cite: 21].

Note: Physical properties reflect typical test values from the manufacturer's TDS (Revision Date: January 25, 2025)[cite: 21].